Niobium-containing tantalum is tantalum minerals iron and pyrochlore. Tantalum and niobium ore containing tantalum and more is called tantalite, niobium many called columbite.
The coltan and pyrochlore can be collected by a cationic collector , and an anionic collector can also be used. The flotation effect is better with a complex collector (such as sodium hydroxy citrate).
Using oleic acid as a collector, the strontium ore is best in the pH range of 6-8, and the coltan and coltan are inhibited in the acidic medium, while quartz , feldspar and dolomite are The planktonic properties are not good at any pH. Therefore, when pH=6-8, oleic acid is used as a collector, and it is easy to separate the gangue from quartz and other gangue.
After treating the antimony ore with 10% acid (sulfuric acid), it becomes easy to float. With the increase of the amount of acid, the floatability of the antimony ore is increased, and the effect of using sulfuric acid is better than that of using hydrochloric acid. Treatment with 1% hydrofluoric acid is similar to sulfuric acid.
When oleic acid is used as a collector and the concentration of sodium sulfide is 10-20 mg/l, the antimony ore and part of the gangue can be suppressed. When a cationic collector is used, sodium sulfide initially activates some minerals such as antimony ore, but as its amount increases, the recovery of antimony ore decreases. When lanthanum is used to capture bismuth ore, a small amount of sodium silicate can suppress all minerals.
Wear-resisting Steel Plate is composed of low Carbon Steel Plate and alloy wear-resisting layer. When working, the matrix provides comprehensive properties such as strength, toughness and plasticity of resisting external forces, and the alloy wear-resistant layer provides wear-resistant properties that meet the requirements of specified working conditions.
Wear-resisting steel alloy wear-resisting layer and base plate are metallurgical combination. By means of special equipment and automatic welding process, the high-hardness self-protecting alloy wire is uniformly welded on the substrate, and the composite layers are one to two or even more. In the composite process, due to the different shrinkage ratio of the alloy, uniform transverse cracks appear, which is a significant feature of the wear-resistant steel plate.
Abrasion Resistant Steel Plate,Wear Resistant Steel Plate,Alloy Wear Resistant Steel Plate,Abrasion Carbon Steel Plate
SHANDONG HUITONG STEEL CO.,LTD , https://www.cnmetalsupply.com